er70s 6 shielding gas

Field Notes: AWS E7018 Universal Carbon Steel Welding Rods, Tested and Talked About I spent a week back-and-forth between a fab shop and a hydro test yard to revisit the aws e7018 welding rod from Jinlong (CB-J508). To be honest, it’s a crowded category, but this one has two things going for it: predictable arc starts on AC or DC+, and the kind of low-hydrogen coating that doesn’t drive inspectors crazy. What it is (and where it comes from) Product: AWS E7018 Universal Carbon Steel Welding Rods 2.5–5.0 mm. Origin: Liusu Industrial Area, Dingzhou City, Hebei, China. The CB-J508 is a low hydrogen potassium-type coated electrode—AC/DC dual-use—with a stable arc, easy slag release, small spatter, attractive bead profile, decent low-temp toughness, and crack resistance. Pricing is quoted FOB at around US $0.5–9,999 per piece, MOQ ≈100 pieces, monthly supply ≈10,000 pieces. Yes, that range is wide—depends on diameter, packaging, and any private-label work. Spec snapshot Classification AWS A5.1 E7018; ISO 2560-A approx. E 42 4 B 42 H5 (real-world use may vary) Diameters 2.5 / 3.2 / 4.0 / 5.0 mm; length ≈300–400 mm Current & Polarity AC or DC+, typical amps: 2.5 mm: 70–100 A; 3.2 mm: 90–130 A; 4.0 mm: 120–170 A; 5.0 mm: 160–220 A Mechanicals (typ.) Tensile ≥490 MPa; Yield ≥400 MPa; Elongation ≈22%; Impact toughness ≈27–47 J @ -30°C Hydrogen Diffusible H8 (some heats H4R with proper baking/handling; verify per batch) Flux Chemistry Low-hydrogen, potassium-activated, iron powder blend Where it fits: applications and industries Structural steel—bridges, columns, heavy frames (A36, A572) Pressure parts and process piping (per WPS qualified to ASME IX) Shipbuilding and offshore modules—toughness matters General repair—farm/earthmoving equipment, crane booms Many customers say it’s forgiving on slightly rust-tinted joints, but, actually, keep prep clean—E7018 rewards cleanliness. Process flow and QA (short version) Materials : Low-carbon steel core wire, iron powder, deoxidizers, potassium-based low-hydrogen binders. Methods : Wire drawing → flux coating → controlled drying → packaging with moisture barriers. Baking/handling : Re-bake 300–350°C for 1–2 h; hold at ≈120°C in a rod oven; exposure limit typically 4 h (shop rules vary). Testing : Mechanical tests per AWS A5.1; hydrogen per AWS A4.3; WPS/PQR per ASME IX. Service life : Shelf ≈12 months sealed; after opening, manage moisture religiously, or re-bake. Vendor comparison (quick take) Vendor/Model Positioning Hydrogen/Coating AC Performance Jinlong CB‑J508 (this aws e7018 welding rod ) Cost-effective; OEM/private label options Low hydrogen, potassium; H8 typical Stable on AC 50/60 Hz ESAB OK 48.00 Global benchmark in many yards Often rated H4R Strong AC/DC performance Lincoln Excalibur 7018 MR Moisture-resistant variant H4R with MR packaging Smooth arc, easy restarts Note: Comparison based on publicly available data and shop-floor evaluations; always confirm to your project spec. Customization and supply Jinlong offers dia/length mixes, private labeling, and packaging tweaks (vac-seal, tin, carton). Lead times are reasonable—supply ability ≈10k pieces/month. MOQ starts around 100 pieces. If your procedure needs H4 or specific impact values, ask for batch certs and heat-specific rebake guidance. In the field: two quick case notes 1) Bridge fab, 345 MPa plate: Welders liked the arc on older AC tappers; NDT team reported fewer slag inclusions vs. their previous brand—repair rate dropped ~15% over three weeks. 2) Process piping spools (P-No. 1): After a 350°C rebake, coupons met tensile and bend per AWS A5.1; RT acceptance improved to 98% on one line-up. Small sample, but encouraging. Tips and caveats Preheat per base metal thickness and spec—don’t rely on “7018 forgiveness.” Keep stubs dry; moisture is the silent killer of low-hydrogen procedures. Qualify WPS/PQR to ASME IX or equivalent before production. No shortcuts. If your spec calls for H4R, verify packaging and test reports for the batch. Bottom line: This aws e7018 welding rod hits the practical middle ground—cost, availability, and dependable AC/DC behavior. For critical work, tighten handling and demand test certs; for general steel fab, it’s a solid, shop-friendly stick. References AWS A5.1/A5.1M: Specification for Carbon Steel Electrodes for Shielded Metal Arc Welding AWS A4.3: Standard Methods for Determination of Diffusible Hydrogen in Steel Weld Metal ISO 2560-A: Welding consumables — Covered electrodes for manual metal arc welding of non-alloy and fine grain steels ASME BPVC Section IX: Welding Qualifications